Aluminium 5083 h111 and Al 5754 h22 Properties

5083 aluminum plate belongs to Al-Mg alloy with the main alloying element Mg and a small amount of other elements such as silicon (Si). For example, the maximum content of silicon is usually no more than 0.40%. Its common tempers are H111, H112, H116, H321, etc.

Aluminium 5083 h111 is suitable for products that have undergone a moderate amount of work hardening after final annealing, but the degree of work hardening is not as good as that of the H11 temper. The 5083H112 temper is suitable for the free processing state of hot-rolled plates and hot-processed products.

5083-O and 5083-h111 aluminum sheethas a sufficient market practice basis as a powder tanker tank material in European powder tankers. Compared with steel trailers, aluminum alloy trailers can effectively achieve overall lightweighting of the vehicle, improve load-bearing performance, and improve transportation efficiency.

The common width of 5083 ultra-wide aluminum plates purchased by tank truck companies is 2.2 meters, and the thickness is 5mm, 6mm, 7mm, 8mm. A tank truck is usually made of 4-6 ultra-wide aluminum plates. In recent years, government departments have increased their advocacy for all-aluminum tank trucks and environmental requirements for energy conservation and emission reduction, and the demand for 5083 ultra-wide aluminum plates is further increasing.

5754 aluminum alloy is a kind of material for making tank cars. It is a typical alloy in the Al-Mg alloy system and contains 2.6-3.6% magnesium. The commonly used tempes are Al 5754 h22,H12, H14, H114, etc. 5754 medium and thick plates have the characteristics of medium strength, good corrosion resistance, weldability and easy processing and forming.

At 320℃ ~ 340℃, the 5754 aluminum undergoes partial recrystallization, the strength decreases rapidly, and the elongation increases; after annealing at 330℃ for 3min, the material's tensile strength, yield strength, and elongation are 250MPa, 150MPa, and 15.4%, respectively. This process can be used to guide the production of 5754-H22 state products on the continuous annealing line.

Haomei Aluminum can produce 5083 and 5754 aluminum sheets in different tempers with a thickness range of 0.15-600mm, a width range of 20-2650mm, and a length range of 500-16000mm, to meet the diverse needs of different customers. Welcome to leave message below to inquire what you need.